[1]齐武a,张云莲b,彭建庭a.混杂来源再生混凝土的抗压强度及衍射分析[J].浙江科技大学学报,2017,(05):366-370.[doi:10.3969/j.issn.1671-8798.2017.05.008 ]
　QI Wua,ZHANG Yunlianb,PENG Jiantinga.Analysis on compressive strength and XRD of recycled concrete with blended-source recycled aggregate[J].,2017,(05):366-370.[doi:10.3969/j.issn.1671-8798.2017.05.008 ]
点击复制

混杂来源再生混凝土的抗压强度及衍射分析(/HTML)
分享到：

《浙江科技大学学报》[ISSN:2097-5236/CN:33-1431/Z]

卷:
期数:
2017年05期
页码:
366-370
栏目:
出版日期:
2017-11-09

文章信息/Info

Title:
Analysis on compressive strength and XRD of recycled concrete with blended-source recycled aggregate
文章编号:
1671-8798(2017)05-0366-05
作者:
齐武a; 张云莲b; 彭建庭a
浙江科技学院 a.土木与建筑工程学院; b.中德工程师学院,杭州 310023
Author(s):
QI Wua;  ZHANG Yunlianb;  PENG Jiantinga
a.School of Civil Engineering and Architecture; b.Chinese-German Institute of Applied Engineering, Zhejiang University of Science and Technology,Hangzhou 310023,Zhejiang, China
关键词:
再生骨料混凝土;  混杂骨料;  单一骨料;  抗压强度;  X射线衍射分析
分类号:
TU528
DOI:
10.3969/j.issn.1671-8798.2017.05.008
文献标志码:
A
摘要:
利用混杂来源再生骨料(混杂骨料)和单一来源再生骨料(单一骨料)逐步替代天然骨料,讨论不同水灰质量比下再生骨料掺量对再生混凝土抗压强度的影响,并结合X射线衍射方法,分析混杂再生混凝土不同龄期的水化程度。试验结果表明:随着混杂骨料掺量从0%到100%逐步增加,水灰质量比为0.50、0.55、0.60的3组混杂再生混凝土的抗压强度均迅速降低,其中水灰质量比为0.55的试件组降低速率最小; 混杂骨料掺量为100%时,在所测试龄期范围内,再生混凝土抗压强度比未掺再生骨料的空白试件降低了18.7%～33.2%。水灰质量比同为0.55时,混杂再生骨料混凝土的抗压强度均低于同条件下单一再生混凝土的抗压强度; 掺量较少时,混杂骨料和单一骨料来源问题对再生混凝土的早期抗压强度影响不大,但达75%大掺量后对再生混凝土的后期抗压强度有明显影响。X射线衍射分析表明,混杂再生骨料中含有较多的C3S和C2S熟料组分,其活性较低,这导致掺加再生骨料后混凝土强度的降低。

参考文献/References:

[1] 秦中伏,孙楠楠,温海珍.再生骨料混凝土的应用现状与研究进展[J].材料导报,2013,27(23):142.
[2] 肖建庄,李佳彬,兰阳.再生混凝土技术研究最新进展与评述[J].混凝土,2003(10):17.
[3] ZHOU C H, CHEN Z P. Mechanical properties of recycled concrete made with different types of coarse aggregate[J]. Construction and Building Materials,2017,134:497.
[4] 韩帅.再生粗骨料品质和取代率对再生混凝土耐久性能的影响[D].青岛:青岛理工大学,2015.
[5] 王晓飞,李秋义,罗健林,等.不同品质再生粗骨料混凝土的力学性能及鲍罗米公式拟合[J].混凝土,2016(3):60.
[6] 曹剑.再生粗骨料品质和取代率对再生混凝土抗冻性能的影响[J].青岛理工大学学报,2016(4):17.
[7] 李秋义,全洪珠,秦原.混凝土再生骨料[M].北京:中国建筑工业出版社,2011.
[8] 肖建庄,雷斌,袁飚.不同来源再生混凝土抗压强度分布特征研究[J].建筑结构学报,2008,29(5):94.
[9] 黄滔,彭小芹,王开宇,等.不同来源再生粗集料对再生混凝土性能的影响[C]//房建材料与绿色建筑.北京:中国建材工业出版社,2009.
[10] ARORA S, SINGH S P. Analysis of flexural fatigue failure of concrete made with 100% coarse recycled concrete aggregates[J]. Construction and Building Materials,2016,102:782.
[11] KISKU N, JOSHI H, ANSARI M, et al. A critical review and assessment for usage of recycled aggregate as sustainable construction material[J]. Construction and Building Materials,2017,131:721.
[12] LOTFI S, EGGIMANN M, WAGNER E, et al. Performance of recycled aggregate concrete based on a new concrete recycling technology[J]. Construction and Building Materials,2015,95:243.
[13] KUMAR R. Influence of recycled coarse aggregate derived from construction and demolition waste(CDW)on abrasion resistance of pavement concrete[J].Construction and Building Materials,2017,142:248.
[14] 李军涛,陈宇良,陈宗平,等.不同骨料来源再生混凝土常规三轴受压性能研究[J].混凝土,2015(2):65.
[15] 王怀亮,张楠.改性再生骨料对自密实混凝土性能的影响[J].哈尔滨工业大学学报,2016,48(6):150.
[16] 崔正龙,童华彬,吴翔宇.再生粗骨料的形态及性质对混凝土力学性能影响研究[J].硅酸盐通报,2014,33(9):2429.
[17] 中华人民共和国住房和城乡建设部.普通混凝土配合比设计规程:JGT 55—2011[S].北京:中国建筑工业出版社,2011.
[18] 肖建庄,李佳彬,孙振平,等.再生混凝土的抗压强度研究[J].同济大学学报(自然科学版),2004,32(12):1558.
[19] 张学元.再生骨料在高性能混凝土中的应用研究[J].混凝土,2017(2):87.
[20] 霍洪媛,范程程,陈爱玖,等.不同强度等级的再生骨料对再生混凝土基本力学性能影响[J].混凝土,2017,328(2):60.

备注/Memo

备注/Memo:
收稿日期: 2017-03-18
基金项目: 浙江科技学院学科交叉预研专项项目(2013JC08Y)
通信作者: 张云莲(1968— ),女,浙江省浦江人,教授,博士,主要从事高性能水泥基材料研究。E-mail:qinger0302@aliyun.com。
更新日期/Last Update: 1900-01-01